Q1: What is PRS-P-C01 HT Glass Ceramic(Press)? What does HT/LT/MT/MO mean?
A: PRS-P-P01 is HT Press 10 colors high-transparency as image: LT? Actually HT 10 colors image shows 10 colors high-transparency for press, ideal for ultra-thin veneers, minimal reaction layer, no chipping, natural color. Technical density 2.4-2.6, flexural ≥420 MPa, thermal (10±0.5)x10-6, Sintering temperature: 920±10℃, solubility <100, radioactivity ≤1.0. Pair with G01-G20 low-temp 750-800C G19 FP G20. Model code PRS-S-C01 per zonmedtech.com as per your screenshots 23:16. HT Press 10 colors high-transparency as image: LT? Actually HT 10 colors image shows 10 colors high-transparency for press, ideal for ultra-thin veneers, minimal reaction layer, no chipping, natural c
Q2: What are shades/colors for PRS-P-P01? How many colors?
A: Per image: HT Press 10 colors as shown: PRS-P-P01 HT Glass Ceramic(Press) – 10 COLORS High-Transparency Press – Firing Surface Lustre Optical Mimicry Natural Aesthetics Structural Integrity. For detailed Vita shades A1-D4 BL1-BL4 MOX0 HOX0 MOX1. Natural color shade excellent aesthetic effect.
Q3: What are technical data and features for PRS-P-P01? Strength?
A: Technical per previous glass ceramic data: CAD biaxial flexural strength ≥480 MPa, PRESS ≥420 MPa, Density 2.4-2.6 g/cm3 after sintering 2.4-2.7, Thermal Expansion (10±0.5)x10-6 K-1, Sintering temperature: 920±10℃, Chemical <100 ug/cm2, Radioactivity ≤1.0 Bq/g. Features: High Strength Toughness Natural Aesthetic Precise CAD Processing Wide Clinical Excellent Bonding for CAD, Natural Color Minimal Reaction Layer No Chipping Ultra-Thin Veneer Acid Stain Resistance for PRESS.
Q4: Can PRS-P-P01 be stained with CERAMIX STAIN G01-G20 low-temp glaze paste? Is it matched system?
A: Yes complete matched own system: Own PRS-S-P01 PRS-P-C/P glass ceramic + own CERAMIX STAIN G01-G20 low-temp glaze paste 730-800C. G01 Bright Red G02 Dark Red G03 Pink G04 Light Pink gum, G05 Sepia G06 Bronze G07 Khaki G08 Orange G09 Yellow G10 Green G11 Dark Green G12 Dark Blue G13 Light Blue G14 Lilac G15 Black G16 Gray G17 Beige G18 White characterization, G19 Glaze FP fluorescence paste for anterior fluorescence, G20 Glaze non-fluorescence for posterior. Low-temp firing does not affect glass ceramic strength.
Q5: When to choose PRS-P-P01 vs other models? Application?
A: Choose PRS-P-P01 based on translucency needed: HT high-transparency for ultra-thin veneers highly aesthetic, LT low-transparency for crowns more opacity, MT medium-transparency balanced, MO/HO opaque for masking dark stumps. Per your site: Firing Surface Lustre Optical Mimicry Natural Aesthetics Structural Integrity. Own system PRS-P-C/P + G01-G20 closed loop.