LT CAD Low-Transparency as image LT Glass Ceramic(CAD) PRS-P-C03, low-transparency CAD block, features Max Masking Max Strength Durability Firing Glass-Ceramic Pressable Ceramic per tags, for crowns needing strength and masking. Technical ≥480 MPa. Pair with G01-G20.
Q1: What is PRS-P-C03 LT Glass Ceramic(CAD)? What does HT/LT/MT/MO mean?
A: PRS-P-C03 is LT CAD Low-Transparency as image LT Glass Ceramic(CAD)PRS-P-C03, low-transparency CAD block, features Max Masking Max Strength Durability Firing Glass-Ceramic Pressable Ceramic per tags, for crowns needing strength and masking. Technical ≥480 MPa. Pair with G01-G20. Model code PRS-P-C03 per zonmedtech.com as per your screenshots 23:16. LT CAD Low-Transparency as image LT Glass Ceramic(CAD) PRS-S-P03, low-transparency CAD block, features Max Masking Max Strength Durability Firing Glass-Ceramic Pressable Ceramic per tags, for crowns n
Q2: What are shades/colors for PRS-P-C03? How many colors?
A: Per image: Multiple shades colors as shown: PRS-P-C03 LT Glass Ceramic(CAD) – Low-Transparency CAD – Firing Durability Max Masking Max Strength Glass-Ceramic Pressable Ceramic. For detailed Vita shades A1-D4 BL1-BL4 MOX0 HOX0 MOX1. Natural color shade excellent aesthetic effect.
Q3: What are technical data and features for PRS-P-C03? Strength?
A: Technical per previous glass ceramic data: CAD biaxial flexural strength ≥480 MPa, PRESS ≥420 MPa, Density 2.4-2.6 g/cm3 after sintering 2.4-2.7, Thermal Expansion (10±0.5)x10-6 K-1, Transition Temperature 820±20°C, Chemical <100 ug/cm2, Radioactivity ≤1.0 Bq/g. Features: High Strength Toughness Natural Aesthetic Precise CAD Processing Wide Clinical Excellent Bonding for CAD, Natural Color Minimal Reaction Layer No Chipping Ultra-Thin Veneer Acid Stain Resistance for PRESS.
Q4: Can PRS-P-C03 be stained with CERAMIX STAIN G01-G20 low-temp glaze paste? Is it matched system?
A: Yes complete matched own system: Own PRS-P-C03 PRS-P-C/P glass ceramic + own CERAMIX STAIN G01-G20 low-temp glaze paste 730-800C. G01 Bright Red G02 Dark Red G03 Pink G04 Light Pink gum, G05 Sepia G06 Bronze G07 Khaki G08 Orange G09 Yellow G10 Green G11 Dark Green G12 Dark Blue G13 Light Blue G14 Lilac G15 Black G16 Gray G17 Beige G18 White characterization, G19 Glaze FP fluorescence paste for anterior fluorescence, G20 Glaze non-fluorescence for posterior. Low-temp firing does not affect glass ceramic strength.
Q5: When to choose PRS-P-C03 vs other models? Application?
A: Choose PRS-P-C03 based on translucency needed: HT high-transparency for ultra-thin veneers highly aesthetic, LT low-transparency for crowns more opacity, MT medium-transparency balanced, MO/HO opaque for masking dark stumps. Per your site: Firing Durability Max Masking Max Strength Glass-Ceramic Pressable Ceramic. Own system PRS-P-C/P + G01-G20 closed loop.