PRS-S-F01
Color:
- White Paste
Specification:
- 14g / Syringe
Holding/Peak Time：
- 1-2 mins
Firing Temperature：
- 700°C – 900°C
Compatible Substrates：
- Lithium Disilicate, Glass Ceramic
Certification：
- MDR
- ISO13485
Key Features
PRS-S-F01 Firing Paste | Professional Dental Sintering & Retention Material. Formulated specifically to support and stabilize dental restorations during the firing process, PRS-S-F01 is a premium white firing paste engineered to prevent deformation and ensure even heat distribution. Its smooth, non-slumping consistency allows dental technicians to securely position crowns, bridges, and veneers on firing trays, delivering reliable performance and flawless aesthetic results without contaminating the restoration
- Superior Shape Stability
- Easy Application & Removal
- Non-Contaminating Formula
- Secure Support
- Universal Compatibility
- Optimal Thermal Resistance
Product Performance
| Parameter | Specification |
|---|---|
| Product Type | Aesthetic Sintering |
| Density | 2.4–2.6 / cm³ |
| Radioactivity | ≤1.0Bq/g |
| Firing Temperature | 730-890℃ |
| Holding Time | 1-2min |
| Chemical Solubility | < 100ug/cm³ |
| Transition Temperature | 1480–1550℃ |
| Biaxial Flexural Strength | ≥90MPa |
| Thermal Expansion Coefficient | (9.5±0.5)×10⁻⁶ K⁻¹ |
| Transparency | Natural Esthetic |
Process Description
Ensure the application surface is clean, dry, and free of residues. Perform necessary pre-treatment for optimal paste adhesion.
Apply the sintering paste evenly using a suitable instrument to achieve the desired thickness, contour, and seamless integration
Fire in a designated furnace following the specific sintering schedule for the paste and substrate materials
Proof of Performance
Before: Unsupported Sintering (Without High-Viscosity Paste