PRS-S-P03
Color:
- A1, A2, A3,A3.5,,A4
- B1, B2, B3, B4
- C1, C2, C3, C4
- D1,D2, D3, D4
- BL1, BL2, BL3, BL4
Specification:
- 5 pieces/box
Pressing Temperature：
- 820±10℃
Certification：
- MDR
- ISO13485
compatibility：
- Compatible with mainstream ceramic press furnaces
Key Features
Zonmed Low-Transparency CAD/CAM Glass Ceramic Blocks (PRS-S-P03) | Enhanced Core-Masking Power. Specially formulated for posterior restorations, bridges, and masking discolored core structures, PRS-S-P03 offers exceptional hiding power combined with high flexural strength. Designed for efficient CAD/CAM milling and subsequent crystallization firing, these low-transparency blocks ensure reliable structural durability and a natural shade match.
- Low-Transparency Design
- Superior Core-Masking Power
- High Flexural Strength & Durability
- Precise Marginal Integrity
- Precise Marginal Integrity
- Ideal for Posterior Crowns & Bridges
Product Performance
| Parameter | Specification |
|---|---|
| Transparency | LT |
| Density | 2.4–2.7 / cm³ |
| Radioactivity | ≤1.0Bq/g |
| Chemical Solubility | < 100ug/cm³ |
| Firing / Pressing Temperature | 820±10℃ |
| Biaxial Flexural Strength | ≥480MPa |
| Thermal Expansion Coefficient | (10±0.5)×10⁻⁶ K⁻¹ |
| Vickers hardness | 5200±200MPa |
Process Description
Place the milled glass ceramic restoration into the dental ceramic furnace and execute the recommended crystallization firing cycle to achieve optimal density, strength, and shade
Complete any required individual staining or glazing for aesthetic enhancement, followed by final high-gloss polishing to deliver a natural, clinical-ready restoration
Complete any required individual staining or crystallization firing, followed by final high-gloss polishing to deliver a natural, clinical-ready restoration.