PRS-S-C02
Color:
- B1、B2
- BL1、BL2、BL3、BL4
- A1、A2、A3、A3.5
Specification:
- 10 pieces/box
Pressing Temperature：
- 920±10℃
Certification：
- MDR
- ISO13485
compatibility：
- Compatible with mainstream ceramic press furnaces
Key Features
Zonmed Low-Translucency Glass Ceramic Blocks (PRS-S-C02-LT) | Enhanced Opalescence. Specially formulated for posterior restorations and masking discolored core structures, PRS-S-C02-LT offers exceptional hiding power combined with high flexural strength. Designed for efficient laboratory pressing, these low-translucency blocks ensure reliable structural durability and a natural shade match for crowns and bridges
- Low-Translucency Design
- Superior Core-Masking Power
- High Flexural Strength & Durability
- Optimized Pressing Flow
- Precise Marginal Integrity
- Ideal for Posterior Crowns & Bridges
Product Performance
| Parameter | Specification |
|---|---|
| Transparency | LT (Low-Transparency) |
| Density | 2.4–2.6 / cm³ |
| Radioactivity | ≤1.0Bq/g |
| Chemical Solubility | < 100ug/cm³ |
| Firing / Pressing Temperature | 920±10℃ |
| Biaxial Flexural Strength | ≥420MPa |
| Thermal Expansion Coefficient | (10±0.5)×10⁻⁶ K⁻¹ |
Process Description
Place the investment ring into the dental ceramic furnace and execute the recommended pressing cycle to ensure optimal density and structural integrity.
Carefully remove the pressed framework from the investment material, performing necessary sandblasting, finishing, and contouring for an ideal marginal fit.
Complete any required individual staining or crystallization firing, followed by final high-gloss polishing to deliver a natural, clinical-ready restoration.